TU 2211-136-05786801-2006
Product obtained by copolymerization of propylene and ethylene in presence of complex metalorganic catalysts.
Chemical name: Propylene and ethylene copolymer Incorporates long-term thermal stability, thermal- oxidative degradation resistance when PP is produced, processed and PP-made articles are exploited, improved optical properties, improved antistatic properties for articles production and improved melt rheology.
Application: short-cycle injection molding, high-quality packaging, transparent containers and covers.
| Value | Test Method | |
|---|---|---|
| 1. Flow-melt index, g/10 min, within the range at 2.16 kg/230°С |
35-45 | ASTM D 1238/L |
| 2. Flexural modulus, MPa, min | 950 | ASTM D 790 |
| 3. Izod impact strength at 23 °C, J/m, min | 45 | ASTM D 256 |
| 4. Tensile strength, MPa, min | Not rated | ASTM D 638 |
| 5. Ultimate tensile elongation, %, min | Not rated | ASTM D 638 |