TU 2211-136-05766801-2006
Product obtained by polymerization of propylene in presence of complexmetalorganic catalysts.
It incorporates long-term thermal stability, thermal-oxidative degradation resistance when PP is produced, processed and PP- made articles are exploited, ambient discoloration resistance, improved melt rheology.
Application: diapers, medical and sanitary fabrics, furniture topping and upholstery, nonwoven fabrics produced frommelt.
| Value | Test Method | |
|---|---|---|
| 1. Flow-melt index, g/10 min, within the range | 20 - 30 | ASTM D 1238/L |
| 2. Flexural modulus, MPa, min | 1050 | ASTM D 790 |
| 3. Izod impact strength at 23 0C, J/m, min | 25 | ASTM D 256 |
| 4. Tensile strength, MPa, min | 29 | ASTM D 638 |
| 5. Ultimate tensile elongation, %, min | 12 | ASTM D 638 |