TU 2211-136-05766801-2006
Product obtained by polymerization of propylene in presence of complexmetalorganic catalysts.
It incorporates increased long-term thermal stability, thermal- oxidative degradation resistance when PP is produced, processed and PP-made articles are exploited.
Application: molded technical and domestic articles, compounding, PPsacks lamination, film.
| Value | Test Method | |
|---|---|---|
| 1. Flow-melt index, g/10 min, within the range | 20 - 30 | ASTM D 1238/L |
| 2. Flexural modulus, MPa, min | 1350 | ASTM D 790 |
| 3. Izod impact strength at 23 0C, J/m, min | 25 | ASTM D 256 |
| 4. Tensile strength, MPa, min | 31 | ASTM D 638 |
| 5. Ultimate tensile elongation, %, min | 11 | ASTM D 638 |