TU 2211-136-05766801-2006
Product obtained by copolymerization of propylene and ethylene in presence of complexmetalorganic catalysts.
It incorporates very highlong-term thermal stability, thermal- oxidative degradation resistance when PP is produced, processed and PP-made articles are exploited, effective nucleation.
Application: compounding, injectionmolding.
| Value | Test Method | |
|---|---|---|
| 1. Flow-melt index, g/10 min, within the range | 15-25 | ASTM D 1238/L |
| 2. Flexural modulus, MPa, min | 850 | ASTM D 790 |
| 3. Izod impact strength, J/m, min at 23 °C at -20 °C at -40 °C |
350 80 - |
ASTM D 256 |
| 4. Tensile strength, MPa, min | Not rated | ASTM D 638 |
| 5. Ultimate tensile elongation, %, min | Not rated | ASTM D 638 |