TU 2211-136-05766801-2006
Product obtained by copolymerization of propylene and ethylene in presence of complexmetalorganic catalysts.
It possesses enhanced physical and mechanical characteristics for production of polymeric articles with .ESCR and cold resistance (increased flexural modulus).
Application: packaging, dishware, compounding, automotive parts by injectionmolding.
| Value | Test Method | |
|---|---|---|
| 1. Flow-melt index, g/10 min, within the range | 10-15 | ASTM D 1238/L |
| 2. Flexural modulus, MPa, min | 1300 | ASTM D 790 |
| 3. Izod impact strength at 23 °C, J/m, min at 23 °C at 20 °C |
85 Not rated |
ASTM D 256 |
| 4. Tensile strength, MPa, min | Not rated | ASTM D 638 |
| 5. Ultimate tensile elongation, %, min | Not rated | ASTM D 638 |