TU 2211-136-05766801-2006
Product obtained by copolymerization of propylene and ethylene in presence of complex metalorganic catalysts.
Incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when PP is produced, processed and PP-made articles are exploited, improved antistatic properties to produce articles. Contains a highly effective stabilizer, antistatic, and nucleator in the stabilizer recipe.
Application: packaging, automotive parts by injection molding.
| Value | Test Method | |
|---|---|---|
| 1. Flow-melt index, g/10 min, within the range | 38-50 | ASTM D 1238/L |
| 2. Flexural modulus, MPa, min | 1150 | ASTM D 790 |
| 3. Izod impact strength at 23 °C, J/m, min at 23 °C at 20 °C |
55 Not rated |
ASTM D 256 |
| 4. Tensile strength, MPa, min | Not rated | ASTM D 638 |
| 5. Ultimate tensile elongation, %, min | Not rated | ASTM D 638 |