TU 2211-136-05766801-2006
Product obtained bycopolymerization of propylene and ethylene in presence of complex metalorganic catalysts.
It incorporates very high long-term thermal stability, thermal-oxidative degradation resistance when PP is produced, processed and PP-made articles are exploited.
Application: cell jars, finishing agents for luggage bags, cables, wires.
| Value | Test Method | |
|---|---|---|
| 1. Flow-melt index, g/10 min, within the range | 6.0-9.0 | ASTM D 1238/L |
| 2. Flexural modulus, MPa, min | 1100 | ASTM D 790 |
| 3. Izod impact strength at 23 °C, J/m, min at 23 °C at 20 °C |
90 35 |
ASTM D 256 |
| 4. Tensile strength, MPa, min | 26 | ASTM D 638 |
| 5. Ultimate tensile elongation, %, min | 8 | ASTM D 638 |