TU 2211-145-05766801-2008
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.
Stabilization recipe: antacid, antioxidant, thermostabilizer, processing aid, dispersing agent.
Application: blow molding of articles up to 0.5 dm3.
PE type: High density polyethylene (HDPE)
Chemical name: Ethylene homopolymer
Empirical formula: (-СН2-СН2-)n
| Value | Test Method | |
|---|---|---|
| 1. Density (of base resin), g/cm3, in the range | 0.958 – 0.962 | ASTM D 1505 |
| 2. Melt Flow Rate, g/10 min, in the range: - at 5.0 kg/190°С - at 2.16 kg/190°С |
- 0.4– 0.9 |
ASTM D1238/L |
| 3. Ratio: - MFR 21,6кг / MFR 5 кг - MFR 21,6кг / MFR 2.16 кг |
- above 50 |
ASTM D1238 |
| 4. Flexural Modulus, MPa, min.: | 1400 | ASTM D 790 |
| 5. Izod Impact Strength at 23°С, J/m, min.: | 160 | ASTM D 256 |