TU 2211-145-05766801-2008
Lotrene Q1018N are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer.
They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion or co-extrusion process to modify film properties.
Q1018N are suited for many applications in the field of consumer, agricultural, industrial, food or hygiene packaging, for example: collation shrink, liners, FFS bags, heavy duty sacks, refuse, tunnel films, mulching films.
| Additive Package: | |
|---|---|
| Slip (Erucamide) (ppm) | No |
| Antiblock (ppm) | No |
| Thermal Stabilizers | Yes |
| Value | Test Method | |
|---|---|---|
| 1. Density, g/cm3 | 0.918 | D 792 |
| 2. Melt Flow Index, g/10 min., 190°С / 2,16 kg | 1.0 | D 1238 |
| 3. Crystaline Melting Point, °С | 122 | Internal |
| 4. Vicat Softening point, °С | 100 | D 1525 |
| 5. Tensile Strength @ Yield, MPa: МD TD |
11 11 |
D 882 |
| 6. Tensile Strength @ Break, MPa: МD TD |
38 33 |
D 882 |
| 7. Elongation, %: МD TD |
800 850 |
D 882 |
| 8. Secant modulus @ 1%, MPa МD TD |
215 245 |
D 882 |
| 9. Impact Strength, F 50, g | 150 | D 1709 |
| 10. Tear resistance MD/TD g H/mm |
280/480 70/120 |
D 1922 |
| 11. Haze, % | 11 | D-1003 |
| 11. Gloss (@ 45°) | 60 | D-2457 |